Low-temperature resistance and its temperature dependence in nanostructured silver

Low-temperature resistance and its temperature dependence in nanostructured silver
Low-temperature resistance and its temperature dependence in nanostructured silver
The dc resistance and the temperature coefficient of resistance (TCR) of bulk nanostructured silver (n-Ag), synthesized by inert gas condensation and in situ vacuum compaction as well as by the sol-gel method, was investigated in the temperature range from 4.2 to 300 K. The results indicated that for all of the n-Ag specimens with larger grain sizes (d>20 nm) and higher densities (relative density D>88%) investigated, their resistivity decreased with decreasing temperature, showing metallic behavior; however, it was found that for the n-Ag with smaller grain sizes and lower density (D=45–50 %), the resistance increased with decreasing temperature (negative TCR) as its mean size d<9 nm, exhibiting nonmetallic behavior. Furthermore, it was found that generally at a certain (fixed) temperature (at 280 K, for instance), there were approximately linear relations (with negative slope) between its TCR and reciprocals of both grain size and density. In addition, the absolute magnitudes of the resistivity of n-Ag were higher than that of polycrystalline silver (poly-Ag), and increased with decreasing both grain size and density. With the model of grain boundary reflection, it was evaluated that the electron mean free path at room temperature was 44 and 33 nm for the n-Ag with grain size 38.5 and 25 nm, respectively, both of which are smaller than that of poly-Ag (51 nm). It was also evaluated that the electron transmission coefficient through boundaries decreased monotonically from 0.83 to 0.42 as n-Ag density decreased from 98.5 to 88%, suggesting greater boundary barriers in the n-Ag’s with lower densities. The fact that transition of TCR sign from positive to negative can be attributed mainly to the dominant scattering caused by interfaces as compared to that caused by intragranular phonons in n-Ag with extremely fine grain sizes and low densities.
1550-235X
10596-10604
Qin, X.Y.
7cd0b9e6-43c0-4568-a49b-a64b3dcbb823
Zhang, W.
1c80d4f2-4ba8-41f6-85a6-a76a4d65dc9b
Zhang, L.D.
ac3a34fe-7b32-4194-bc7f-fb0b7cb78316
Jiang, L.D.
418530cb-a31c-46eb-b894-6eda5172b8a2
Qin, X.Y.
7cd0b9e6-43c0-4568-a49b-a64b3dcbb823
Zhang, W.
1c80d4f2-4ba8-41f6-85a6-a76a4d65dc9b
Zhang, L.D.
ac3a34fe-7b32-4194-bc7f-fb0b7cb78316
Jiang, L.D.
418530cb-a31c-46eb-b894-6eda5172b8a2

Qin, X.Y., Zhang, W., Zhang, L.D. and Jiang, L.D. (1997) Low-temperature resistance and its temperature dependence in nanostructured silver. Physical Review B, 56, 10596-10604. (doi:10.1103/PhysRevB.56.10596).

Record type: Article

Abstract

The dc resistance and the temperature coefficient of resistance (TCR) of bulk nanostructured silver (n-Ag), synthesized by inert gas condensation and in situ vacuum compaction as well as by the sol-gel method, was investigated in the temperature range from 4.2 to 300 K. The results indicated that for all of the n-Ag specimens with larger grain sizes (d>20 nm) and higher densities (relative density D>88%) investigated, their resistivity decreased with decreasing temperature, showing metallic behavior; however, it was found that for the n-Ag with smaller grain sizes and lower density (D=45–50 %), the resistance increased with decreasing temperature (negative TCR) as its mean size d<9 nm, exhibiting nonmetallic behavior. Furthermore, it was found that generally at a certain (fixed) temperature (at 280 K, for instance), there were approximately linear relations (with negative slope) between its TCR and reciprocals of both grain size and density. In addition, the absolute magnitudes of the resistivity of n-Ag were higher than that of polycrystalline silver (poly-Ag), and increased with decreasing both grain size and density. With the model of grain boundary reflection, it was evaluated that the electron mean free path at room temperature was 44 and 33 nm for the n-Ag with grain size 38.5 and 25 nm, respectively, both of which are smaller than that of poly-Ag (51 nm). It was also evaluated that the electron transmission coefficient through boundaries decreased monotonically from 0.83 to 0.42 as n-Ag density decreased from 98.5 to 88%, suggesting greater boundary barriers in the n-Ag’s with lower densities. The fact that transition of TCR sign from positive to negative can be attributed mainly to the dominant scattering caused by interfaces as compared to that caused by intragranular phonons in n-Ag with extremely fine grain sizes and low densities.

This record has no associated files available for download.

More information

Published date: 1997

Identifiers

Local EPrints ID: 23568
URI: http://eprints.soton.ac.uk/id/eprint/23568
ISSN: 1550-235X
PURE UUID: a9290793-c140-46d1-8f9a-712006562293

Catalogue record

Date deposited: 31 Jan 2007
Last modified: 15 Mar 2024 06:48

Export record

Altmetrics

Contributors

Author: X.Y. Qin
Author: W. Zhang
Author: L.D. Zhang
Author: L.D. Jiang

Download statistics

Downloads from ePrints over the past year. Other digital versions may also be available to download e.g. from the publisher's website.

View more statistics

Atom RSS 1.0 RSS 2.0

Contact ePrints Soton: eprints@soton.ac.uk

ePrints Soton supports OAI 2.0 with a base URL of http://eprints.soton.ac.uk/cgi/oai2

This repository has been built using EPrints software, developed at the University of Southampton, but available to everyone to use.

We use cookies to ensure that we give you the best experience on our website. If you continue without changing your settings, we will assume that you are happy to receive cookies on the University of Southampton website.

×