The ageing characteristics of an Al-Ag alloy processed by equal-channel angular pressing

The ageing characteristics of an Al-Ag alloy processed by equal-channel angular pressing
The ageing characteristics of an Al-Ag alloy processed by equal-channel angular pressing
An Al–10.8 wt.% Ag alloy was processed by equal-channel angular pressing (ECAP) and aged at temperatures of 373 or 473 K. Hardness measurements were taken after different aging times and the results show the hardness continuously decreases when aging at 473 K but increases to a peak hardness when aging at 373 K. For aging at 473 K, it is shown that metastable ??-phase particles form within the grains and stable ?-phase particles form throughout the sample but these particles make no contribution to the hardness. By contrast, aging at 373 K leads to the formation of stable ?-phase particles on the grain boundaries and a fine dispersion of ?-zones and plate-like ??-phase particles within the grains: the increase in hardness is attributed to these finely-dispersed particles. Aging at 373 K for 100 h, corresponding to peak aging, gives an increase in the uniform elongation in tensile testing and the same high level of stress as in samples after ECAP processing.
aging, aluminium alloys, equal-channel angular pressing, precipitation, metastable phases
0921-5093
240-247
Ohashi, Kunihiro
672fc5e4-c9da-4f17-b6b6-b7dae56f0510
Fujita, Takeshi
f2d5a9fe-84e7-47c2-9e96-7ad57035c7e7
Kaneko, Kenji
59fbdb7b-cec8-4d21-a877-4a6c24084b63
Horita, Zenji
011521b8-3b29-494b-bf3f-346827ddbcce
Langdon, Terence G.
86e69b4f-e16d-4830-bf8a-5a9c11f0de86
Ohashi, Kunihiro
672fc5e4-c9da-4f17-b6b6-b7dae56f0510
Fujita, Takeshi
f2d5a9fe-84e7-47c2-9e96-7ad57035c7e7
Kaneko, Kenji
59fbdb7b-cec8-4d21-a877-4a6c24084b63
Horita, Zenji
011521b8-3b29-494b-bf3f-346827ddbcce
Langdon, Terence G.
86e69b4f-e16d-4830-bf8a-5a9c11f0de86

Ohashi, Kunihiro, Fujita, Takeshi, Kaneko, Kenji, Horita, Zenji and Langdon, Terence G. (2006) The ageing characteristics of an Al-Ag alloy processed by equal-channel angular pressing. Materials Science and Engineering: A, 437 (2), 240-247. (doi:10.1016/j.msea.2006.08.024).

Record type: Article

Abstract

An Al–10.8 wt.% Ag alloy was processed by equal-channel angular pressing (ECAP) and aged at temperatures of 373 or 473 K. Hardness measurements were taken after different aging times and the results show the hardness continuously decreases when aging at 473 K but increases to a peak hardness when aging at 373 K. For aging at 473 K, it is shown that metastable ??-phase particles form within the grains and stable ?-phase particles form throughout the sample but these particles make no contribution to the hardness. By contrast, aging at 373 K leads to the formation of stable ?-phase particles on the grain boundaries and a fine dispersion of ?-zones and plate-like ??-phase particles within the grains: the increase in hardness is attributed to these finely-dispersed particles. Aging at 373 K for 100 h, corresponding to peak aging, gives an increase in the uniform elongation in tensile testing and the same high level of stress as in samples after ECAP processing.

This record has no associated files available for download.

More information

Published date: 2006
Keywords: aging, aluminium alloys, equal-channel angular pressing, precipitation, metastable phases
Organisations: Engineering Mats & Surface Engineerg Gp

Identifiers

Local EPrints ID: 43708
URI: http://eprints.soton.ac.uk/id/eprint/43708
ISSN: 0921-5093
PURE UUID: 07d2c886-6f85-4645-bf31-6fe1b32f7636
ORCID for Terence G. Langdon: ORCID iD orcid.org/0000-0003-3541-9250

Catalogue record

Date deposited: 29 Jan 2007
Last modified: 16 Mar 2024 03:28

Export record

Altmetrics

Contributors

Author: Kunihiro Ohashi
Author: Takeshi Fujita
Author: Kenji Kaneko
Author: Zenji Horita

Download statistics

Downloads from ePrints over the past year. Other digital versions may also be available to download e.g. from the publisher's website.

View more statistics

Atom RSS 1.0 RSS 2.0

Contact ePrints Soton: eprints@soton.ac.uk

ePrints Soton supports OAI 2.0 with a base URL of http://eprints.soton.ac.uk/cgi/oai2

This repository has been built using EPrints software, developed at the University of Southampton, but available to everyone to use.

We use cookies to ensure that we give you the best experience on our website. If you continue without changing your settings, we will assume that you are happy to receive cookies on the University of Southampton website.

×