This data file contains the information about the figure 1,figure 2a,figure 2 b figure 3, figure 4, figure 5

Figure 1		Electrodeposition of PbO2 from a solution containing 1 mol L-1 Pb (CH3SO3)2 and 0.2 mol L-1 MSA at 2.5 A and 60°C for 30 min in a small undivided glass cell containing 100 mL of electrolyte with constant stirring at 700 rpm.

Figure 2 a		Schematic diagram of cell for deposition of TiNS suspension containing 100 mL of TiNS exfoliated with tetrabutylammonium hydroxide (TBAOH) at 
			25 °C.	
Figure 2 b		Schematic diagram of the arrangement for Photocatalytic decolorization of the dye.

Figure 3	FESEM Images of TiNS/PbO2 coatings over the RVC substrate obtained by electrodeposition and anodic electrophoretic deposition (a) RVC strut coated with PbO2 after anodic electrodeposition (b) PbO2 film at higher magnification c) TiNS/PbO2 /RVC layer showing fully covered layer of TiNS film over PbO2 / RVC (d) TiNS/PbO2/RVC layer at higher magnification (e) TiNS/PbO2/RVC at 30,000 magnification at a scale of 100 nm.
Figures 4	(a) TiNS/ PbO2/RVC after calcination at 450 oC (b) calcined TiNS/PbO2/RVC layer having undulated surfaces at higher magnification.
Figure 5	EDX images for elemental analysis of calcined TiNS/PbO2/RVC obtained by Anodic electrophoretic deposition (a) calcined TiNS/PbO2/RVC (b) Titanium elemental analysis (c) Lead elemental analysis (d) Carbon (RVC) elemental analysis.