This thesis investigates the electrodeposition and characterization of zinc-nickel (Zn-Ni) coatings, focusing on the enhancement of adhesion and corrosion resistance by optimizing deposition parameters, anode materials, and post-deposition treatments. Zn-Ni coatings, containing 10–15 wt% Ni, offer superior corrosion resistance compared to pure zinc, making them an effective alternative to cadmium-based coatings.
The effects of different anode materials (zinc, nickel, platinum, 1020 steel, and stainless steel) on coating properties were studied, including voltage behaviour, microstructure, Ni content, and corrosion resistance. Coatings from zinc and nickel anodes exhibited consistent thicknesses of 13–15 µm, with zinc anodes achieving a Ni content of 13.5 wt%, whereas coatings from steel-based anodes were significantly thicker, reaching up to 33 µm, but with lower Ni content (~7 wt%). The coatings from zinc and nickel anodes exhibited fewer defects and minimal porosity, while those from steel-based anodes displayed higher porosity and more irregular surface morphologies. In terms of corrosion resistance, zinc anodes coatings exhibited a lower corrosion rate of 0.44 mm/year compared to 1.54 mm/year for nickel anodes coatings.
The study also investigated the influence of saccharin concentrations on coating properties. Saccharin concentrations up to 1 g/L significantly improved adhesion by producing dense, defect-free coatings. The surface roughness was reduced to 0.897 µm, compared to over 1.7 µm in coatings without saccharin. EDS analysis revealed that the oxygen content was reduced to 1.1 wt% in saccharin-enhanced coatings. High saccharin concentrations also led to a reduction in grain size, but excessive grain refinement resulted in lower hardness, following an inverse Hall-Petch relationship.
Post-deposition heat treatment at 200°C further improved adhesion by promoting atomic diffusion and healing interfacial voids, enhancing the structural integrity of the coatings. The study also explored the use of Ni-Sn interlayers to improve adhesion. Coatings with Ni-Sn interlayers exhibited superior bonding compared to those with pure Ni interlayers, particularly after heat treatment. The Sn content in the interlayer decreased from 7.9 wt% to 5.8 wt% during heat treatment, which improved the interfacial cohesion by reducing oxidation-related brittleness. SEM analysis confirmed that the Ni-Sn interlayers provided a more cohesive interface, minimising voids and cracks even under thermal conditions.
University of Southampton
Yi, Lijia
2ba0112c-e6dd-495d-8559-775bdb6ced05
Yi, Lijia
2ba0112c-e6dd-495d-8559-775bdb6ced05
Wang, Shuncai
8a390e2d-6552-4c7c-a88f-25bf9d6986a6
Wood, Robert
d9523d31-41a8-459a-8831-70e29ffe8a73

Yi, Lijia (2025) Electrodeposited Zn-Ni coatings for the replacement of cadmium. University of Southampton, Doctoral Thesis, 181pp.

Record type: Thesis (Doctoral)

Abstract

This thesis investigates the electrodeposition and characterization of zinc-nickel (Zn-Ni) coatings, focusing on the enhancement of adhesion and corrosion resistance by optimizing deposition parameters, anode materials, and post-deposition treatments. Zn-Ni coatings, containing 10–15 wt% Ni, offer superior corrosion resistance compared to pure zinc, making them an effective alternative to cadmium-based coatings.
The effects of different anode materials (zinc, nickel, platinum, 1020 steel, and stainless steel) on coating properties were studied, including voltage behaviour, microstructure, Ni content, and corrosion resistance. Coatings from zinc and nickel anodes exhibited consistent thicknesses of 13–15 µm, with zinc anodes achieving a Ni content of 13.5 wt%, whereas coatings from steel-based anodes were significantly thicker, reaching up to 33 µm, but with lower Ni content (~7 wt%). The coatings from zinc and nickel anodes exhibited fewer defects and minimal porosity, while those from steel-based anodes displayed higher porosity and more irregular surface morphologies. In terms of corrosion resistance, zinc anodes coatings exhibited a lower corrosion rate of 0.44 mm/year compared to 1.54 mm/year for nickel anodes coatings.
The study also investigated the influence of saccharin concentrations on coating properties. Saccharin concentrations up to 1 g/L significantly improved adhesion by producing dense, defect-free coatings. The surface roughness was reduced to 0.897 µm, compared to over 1.7 µm in coatings without saccharin. EDS analysis revealed that the oxygen content was reduced to 1.1 wt% in saccharin-enhanced coatings. High saccharin concentrations also led to a reduction in grain size, but excessive grain refinement resulted in lower hardness, following an inverse Hall-Petch relationship.
Post-deposition heat treatment at 200°C further improved adhesion by promoting atomic diffusion and healing interfacial voids, enhancing the structural integrity of the coatings. The study also explored the use of Ni-Sn interlayers to improve adhesion. Coatings with Ni-Sn interlayers exhibited superior bonding compared to those with pure Ni interlayers, particularly after heat treatment. The Sn content in the interlayer decreased from 7.9 wt% to 5.8 wt% during heat treatment, which improved the interfacial cohesion by reducing oxidation-related brittleness. SEM analysis confirmed that the Ni-Sn interlayers provided a more cohesive interface, minimising voids and cracks even under thermal conditions.

Text
Electrodeposited Zn-Ni Coatings for the Replacement of Cadmium - Version of Record
Available under License University of Southampton Thesis Licence.
Download (6MB)
Text
Final-thesis-submission-Examination-Miss-Lijia-Yi
Restricted to Repository staff only

More information

Published date: April 2025

Identifiers

Local EPrints ID: 499866
URI: http://eprints.soton.ac.uk/id/eprint/499866
PURE UUID: 33a7884d-490f-4b81-9298-57bc3abdb705
ORCID for Lijia Yi: ORCID iD orcid.org/0009-0006-8459-3596
ORCID for Robert Wood: ORCID iD orcid.org/0000-0003-0681-9239

Catalogue record

Date deposited: 08 Apr 2025 16:31
Last modified: 03 Jul 2025 02:24

Export record

Contributors

Author: Lijia Yi ORCID iD
Thesis advisor: Shuncai Wang
Thesis advisor: Robert Wood ORCID iD

Download statistics

Downloads from ePrints over the past year. Other digital versions may also be available to download e.g. from the publisher's website.

View more statistics

Atom RSS 1.0 RSS 2.0

Contact ePrints Soton: eprints@soton.ac.uk

ePrints Soton supports OAI 2.0 with a base URL of http://eprints.soton.ac.uk/cgi/oai2

This repository has been built using EPrints software, developed at the University of Southampton, but available to everyone to use.

We use cookies to ensure that we give you the best experience on our website. If you continue without changing your settings, we will assume that you are happy to receive cookies on the University of Southampton website.

×